Question 116
Liquid metal embrittlement can occur if 300 Series SS comes in contact with molten _______.
Question 117
Damage from sigma phase appears in the form of ________.
Question 118
Non-stressed relieved __________ is susceptible to stress corrosion cracking when in contact with moist HF vapors in the presence of oxygen.
Question 119
Naphthenic acid corrosion (NAC) is most severe in what phase of flow?
Question 120
A quick test for embrittlement from _________ is a bend test or crush test. Unaffected material will be crushed in a ductile fashion while embrittled components will crack with no signs of ductility.