Question 41

The best way to prevent failures by atmospheric corrosion is to:

A.Shoot all birds that cross the plant fence.

B.Install and maintain appropriate coatings.

C.Build new petrochemical facilities in a dry desert.

D.Reduce airborne particulates.

E.Have an aggressive inspection program.

Question 42

Caustic stress corrosion cracking typically propagates _______ to the weld in adjacent base metal but can occur in the weld deposit or heat affected zone.

A.Perpendicular

B.Transverse

C.Across

D.Parallel

Question 43

Both sulfide stress corrosion cracking and stress-oriented hydrogen-induced cracking are most often found in:

A.Areas where there is significant hydrogen blistering.

B.Steel weldments.

C.Hardened steels.

D.Areas with temperatures above 300°F (149°C).

Question 44

Which of the following is not a method used to prevent brittle fracture?

A.Controlling minimum operating temperatures

B.Thorough inspections

C.Post weld heat treatment

D.Strict controls on selecting construction materials

Question 45

Which of the following is the most significant result of spheroidization in steels?

A.Increased potential for stress corrosion cracking

B.Increased hardness

C.Loss of ductility

D.Loss of strength

Latest Upload: 110PECB.NIS-2-Directive-Lead-Implementer.v2025-12-16.q29; 122SAP.C_C4H32_2411.v2025-12-16.q51; 121Splunk.SPLK-3001.v2025-12-15.q104; 111SAP.C-S4PM2-2507.v2025-12-15.q29; 177APA.FPC-Remote.v2025-12-13.q147; 119CIPS.L6M2.v2025-12-13.q13; 122WGU.Cybersecurity-Architecture-and-Engineering.v2025-12-13.q81; 122Oracle.1Z0-1163-1.v2025-12-13.q17; 149PythonInstitute.PCET-30-01.v2025-12-13.q31; 151API.API-571.v2025-12-13.q120